PU Chemical for Making Shoe Sole of Slippers

Product Details
CAS No.: 9009-54-5
Formula: C3h8n2o
Molecular Principal Chain: Carbon Chain Polymer
  • PU Chemical for Making Shoe Sole of Slippers
  • PU Chemical for Making Shoe Sole of Slippers
  • PU Chemical for Making Shoe Sole of Slippers
  • PU Chemical for Making Shoe Sole of Slippers
  • PU Chemical for Making Shoe Sole of Slippers
  • PU Chemical for Making Shoe Sole of Slippers
Find Similar Products

Basic Info.

Model NO.
HD-8690-3 / HD-2042
Color
White
Transport Package
Various Packages
Specification
18kg/220kg
Trademark
Huide
Origin
Shanghai
HS Code
39095000
Production Capacity
260000 Tons

Product Description

HD-8690-3 / HD-2042
:,
Characteristics: Low density, medium to high hardness.
:,,
Application: For slippers, sandals and casual shoes.
Typical properties of PU resin

Name of products
@40ºC
Appearance
Density
(g/cm3 @40oC)
Viscosity
(mPa·s @40oC)
Package Size
(kg/drum)
HD-8690-3(POL, A)
Cream Liquid
1.03~1.13 1000~3000 18 / 220
HD-2042(ISO, B)
Liquid
1.08~1.20 50~110 20 / 235
Processing
,.60-70ºC(6-10,,).,A..
Please preheat materials at 60~70ºCfor 6~10 hours before processing. Then mix fully the whole drum of POL and other additives according to the following table. Finally, respectively transfer POL and ISO to their corresponding tanks.
HD-8690-3 (POL, A) HD-H/g water/g HD-C008/g HD-C005/g
18 kg(one drum) 600 95 260 80
220 kg (one drum) 7000 1150 3000 800
Reactivity and product performance

Test Items

Reactivity parameters

Test Items

Product performance

Ratio of (A+C) and B material
100/125~130
Moulding density(g/cm3)
0.22~0.28

Material temperature (oC)
38~42/38~42
Hardness(23ºC)
75C~90C
60A~80A

Cream time (s)
5~7
Tensile strength(MPa)
2

End of rise time (s)
20~30
Elongation(%)
100

Free rise density (g/cm3)
0.13~0.16
Tear strength(kN/m)
12

Metal mold temperature (oC)
50~60
Flexing resistance(23ºC)
2
20,000 times no crack

Demould time(min)
2.40~3 DIN
DIN abrasion resistance(mm3)
750
The ratio based on the best value varies with the type and quantity of added paint additives.
The free rise foam density varies with the seasonal variation (temperature, humidity)
Data listed above are just for reference. The detailed data are subjected to practical operation. Please contact us if other physical properties are essential.
PU Chemical for Making Shoe Sole of SlippersPU Chemical for Making Shoe Sole of Slippers

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now