Polyurethane Polymer for Shoe

• Customization: Available
• CAS No.: 9009-54-5
• Formula: C3h8n2o
• Model NO.: HD-6670 / HD-1919
• EINECS: 210-898-8
• Molecular Principal Chain: Carbon Chain Polymer
• Color: White
• Transport Package: Various Package
• Specification: 220kg/235kg
• Trademark: huide
• Origin: China
• HS Code: 3909500000
• Production Capacity: 260000ton

Product Description

HD-6670 / HD-1919
Characteristics: Mid-highhardness, excellent mechanical, cohesive and anti-static properties.
Application: For dual density safety shoe sole production.
Typical properties of PU resin

Name of products	@40ºC Appearance	Density (g/cm^3@40^oC)	Viscosity (mPa·s @40^oC)	Package Size (kg/drum)
HD-6670(POL, A,)	Liquid	1.13~1.18	1000~1500	18 / 220
HD-1919(ISO, B)	Liquid Líquido	1.18~1.20	350~450	20 / 235

Processing
Please preheat materials at 60~70ºCfor 6~10 hours before processing. Then mix fully the whole drum of POL and other additives according to the following table. Finally, respectively transfer POL and ISO to their corresponding tanks.

Type	HD-6670	Hardener/g	water/g	catalyst/g	other
outsole	18 kg(one drum)	0	0~10	220~240	It depends
	220 kg (one drum)	0	0~120	2700~2900	It depends
midsole	18 kg(one drum)	200	30-40	300~320	It depends
	220 kg (one drum)	200	370-490	3700~3900	It depends

Reactivity and product performance

Test Items	Reactivity parameters		Test Items	Product performance
	outsole	midsole		outsole	midsole
Ratio of (A+C) and B material	100:70~73	100:82~85	Moulding density(g/cm^3)	0.80~1.10	0.45~0.55
Material temperature (^oC)	A:40~45 / B:40~45	A:40~45 / B:40~45	Hardness(23ºC,Shore A)	55~65	45~55
Cream time (s)	6~9	5~7	Tensile strength(MPa)	≥8.5	≥4.0
End of rise time (s)	35~45	25~35	Elongation(%)	≥500	≥350
Free rise density (g/cm^3)	0.40~0.70	0.26~0.33	Tear strength(kN/m)	≥30.0	≥20.0
Metal mold temperature (^oC)	45~55	45~55	Flexing resistance 23ºC×2mm×50000times	Crack increase≤4.0mm
Demould time(min)	3~4	3~5	DIN abrasion resistance(mm3)	≤150	/
			Peel strength(KN/m)	≥3.5

The ratio based on the best value varies with the type and quantity of added paint additives.
The free rise foam density varies with the seasonal variation (temperature, humidity)
Data listed above are just for reference. The detailed data are subjected to practical operation. Please contact us if other physical properties are essential.
About Huide

Shanghai Huide Science & Technology Co., Ltd, listed as the second batch of national "Little Giant" enterprises, was established in June 2007 and located in Shanghai Carbon Valley Green Bay Industrial Park (formerly the Jinshan Second Industrial Zone of Shanghai), which was put into production in the second half of 2009. It is a technology-based group company that integrates design, research and development, production, sales and service, and specializes in manufacturing series of new materials such as polyurethane resin ( PU) for synthetic leather,  polyurethane elastomer stock solution, polyester polyol and thermoplastic polyurethane elastomer (TPU). The company has two production bases in Shanghai and Fujian, and its products application covers the daily life fields of shoes, clothing, bags, furniture and transportation industry such as automobiles and railways, the business scope covers production, sales, domestic trade, foreign trade and logistics transportation etc. Approved by the China Securities Regulatory Commission, the company's shares were listed on the Shanghai Stock Exchange on August 28, 2018 with the stock code of 603192 and named as Huide Technology. 


7 Wholly Owned Subsidiaries:

Shanghai Huide International Trade Co., Ltd.
Shanghai Hoard Polyurethane Co., Ltd
Fujian Huide New Material Co., Ltd.
Changzhou Pufeite Chemical Co., Ltd.
Changzhou Yunqi Transportation Co., Ltd.
Shanghai Huide Resin Sales Co., Ltd.
Zhejiang Huide New Material Co., Ltd.